Database of properties for steel and alloy materials worldwide.

 

Properties of LEAN DUPLEX UNS S32101 - ALLOY 1.4162 - LDX 2101

ALLOY 1.4162 / LEAN DUPLEX UNS S32101 / LDX 2101

MATERIAL DESCRIPTION

LDX 2101 is a low Ni-alloyed duplex with balanced chemistry of chromium, molybdenum and nitrogen content to achieve good resistance to localized and uniform corrosion. The duplex microstructure contributes to the high strength and high resistance to stress corrosion cracking. Duplex steels have good weldability. Due to risk of embrittlement, LDX 2101 should not be used at temperatures above 250°C. Very price stable high strength alloy.



LDX 2101 is a low-nickel, nitrogen enhanced lean duplex stainless steel developed for general-purpose use. The austenitic-ferritic (duplex) structure of the alloy is balanced to approximately equal amounts of ferrite and austenite in the solution-annealed condition.

The high chromium and nitrogen content of LDX 2101, combined with an addition of molybdenum, provide very good resistance to localized and uniform corrosion. The duplex microstructure contributes to the alloys high strength and resistance to chloride stress-corrosion cracking. LDX 2101 possesses both superior strength and greater chloride stress-corrosion cracking resistance than conventional 300 series stainless steels.

The corrosion resistance of LDX 2101 is generally good making it suitable for use in a wide variety of applications. In most environments, it is superior to 304L stainless steel and comparable to the molybdenum containing 316L stainless steel.

The enhanced mechanical strength of LDX 2101 is far superior to conventional 300 series stainless steels enabling it to be used in thinner cross-sections which can provide significant cost savings to the end user.

LDX 2101 exhibits good abrasion and erosion resistance and can be fabricated using standard shop practices developed for duplex stainless steels.

APPLICATIONS

The main applications are for details with corrosion resistance better than 304L.

General corrosion is characterized as a uniform attack on a surface in contact with a corrosive medium. The resistance to uniform corrosion in sulfuric acid is shown below. LDX 2101 is superior to 304L and in some cases comparable to 316L.

LDX 2101 is characterized by:

• Ideal for tank production where corrosion strength is sufficient.

• Good resistance to stress corrosion cracking.

• Good resistance to general corrosion.

• High mechanical strength.

• High resistance to erosion corrosion and corrosion fatigue.

Heat Treatment


Solution annealing at 1020 – 1100°C followed by water quenching.

Weldability
Very good.

CHEMICAL COMPOSITION

Weight %

C

Si

Mn

S

P

Cr

Ni

Mo

N

Cu

Min.

4,00

21,00

1,35

0,1

0,20

0,10

Max.

0,040

1,00

6,00

0,015

0,035

22,00

1,90

0,8

0,25

0,80

Product Standards: EN 10088-2, EN 10088–4, ASTM A240, EN ISO 9445-2
Approvals: NACE MR0175/ ISO 15156-3:2015, PED 97/ 23/ EC, CPR 305/ 2011/ EU

MECHANICAL PROPERTIES

Yield strength Rp0.2,
MPa

Tensile strength Rm,
MPa

Elongation
[%]

Hardness
[HB]

Impact, Charpy-V, -40ÂșC
[J]

Pre

Surface

PLATE CR (COIL)

≥ 530

≥ 700

≥ 30

≥ 50

26

2B/2E

PLATE HR (COIL)

≥ 450

≥ 650

≥ 30

≤ 290

≥ 50

26

1D

PLATE (QUARTO)

≥ 450

≥ 650

≥ 30

≤ 290

≥ 27

26

1D

 




Source:

Comments :

0 Comments to “Properties of LEAN DUPLEX UNS S32101 - ALLOY 1.4162 - LDX 2101”

Post a Comment

If you have any questions, concerns, or feedback about our website, our team is always here to assist you.

 
© Copyright 2013 Search Steel