ASTM A276-98b, AISI 440C Stainless Steel Data Sheet: Composition, Applications and Properties

440C Stainless Steel Data Sheet

440C stainless steel is a martensitic grade of stainless steel that provides very good wear resistance combined with moderate corrosion resistance in mild environments. 440C is heat treatable to RC 59. This grade is commonly used in cutlery and food processing applications.
Read more:
440C Stainless steel is a type of modern steel and famous for its high corrosion resistant, wear resistance, strength and hardness qualities among all the stainless alloys, capable of attaining (after heat treatment) the highest hardness (60 HRC). It has good resistance to the atmosphere, fresh water and mild acids. It has best resistance in the hardened, tempered and passivated condition. It allows creating a smooth polished surface and Razor sharp edges. It is being used in cutting instruments, rolling element bearings, valve seats, high quality knife blades, surgical instruments, chisels, ball bearings and valve parts and most commonly used in the production of Cutting tools, including Haircutting Scissors, daggers and swords.
Grades 440A and 440B are identical except for slightly lower carbon contents (0.60 - 0.75% and 0.75 - 0.95% respectively), they attain lower hardness but slightly higher corrosion resistances. Although all three versions of this grade are standard grades, in practice 440C is more available than the A or B variants.
Another alloy 440F (UNS S44020) also exists, with the same high carbon content as 440C.

440C Related Specifications
USA Germany Japan Australia
ASTM A276-98b 440C
SAE 51440C, AISI 440C
UNS S44004
W.Nr 1.4125 X105CrMo17 JIS G4303 SuS 440C AS 2837-1986 440C
Germany: DIN 1.4125
United States: AMS 5618 , AMS 5630 , ASTM A276 , ASTM A314 , ASTM A473 , ASTM A493 , ASTM A580 , FED QQ-S-763 , MIL SPEC MIL-S-862 , SAE 51440C , SAE J405 (51440C) , UNS S44004

Chemical Composition

Carbon 1.00%
Manganese .50%
Chromium 17.50%
Silicon .35%
Molybdenum .50%
Chemical Composition ranges of 440C stainless steel
Grade440C
Ingredients Min. Max.
Carbon 0.95 1.20
Manganese - 1.00
Silicon - 1.00
Phosphorus - 0.040
Sulphur - 0.030
Chromium 16.00 18.00
Molybdenum - 0.75
Iron Balance

 

Typical Applications

Plastic Injection Molds
Cutlery
Custom Knives
Food Processing Equipment
Bearings
Petroleum Pumps and Valves
Surgical Tools

Corrosion Resistance

440C stainless steel is characterised by good corrosion resistance in mild domestic and industrial environments, including fresh water, organic materials, mild acids, various petroleum products. 440C also provides extreme high strength, hardness and wear resistance when in the hardened and tempered condition.

Thermal Treatments

Preheat : Optional preheat stage for unbalanced geometries or complex designs - 1100/1250F (590/675C), equalize, standard preheat stage - 1400/1500F (760/815C), equalize.

Austenize : 1850/1900F (1010/1020C), equalize, 30/45 minutes at temperature.

Quench : Air, positive pressure vacuum to below 125F (50C)(2 bar minimum). Interrupted oil to below 1000F (540C). Air cool to 150F (65C). Temper immediately.

Temper : 400/800F (205/425C), hold 2 hours at temperature, air cool. Temper twice. Avoid tempering between 800 and 1100F, due to a decrease in toughness and corrosion resistance.

Cryogenic Treating : Refrigeration treatments may improve long term dimensional stability by transforming retained austenite. Refrigeration treatments should generally be performed after the first temper, and must be followed by a temper.

Hardness and Impact Toughness Data
Air cooled from 1885F(1030C)
Tempering
TemperatureHardness
Deg. FDeg. CHRC
As quenched59
21210059
40020556
60031554
80042555
100054051

Surface Treatments

Nitriding decreases the corrosion resistance of stainless steels and is generally not recommended for stainless steels.

Annealing

A. Heat to 1650F (870C), hold 2 hours, slow cool 25F (15C)/hour maximum) to 1200F (650C), air cool.
OR
B. Heat to 1600F (870C), hold 2 hours, cool to 1300F (760C), hold 4 hours, air cool.
Typical annealed hardness: 215/255 BHN.

Stress Relieving

Annealed Material: Heat to 1200/1250F(650/675C), hold two hours, cool in still air.
Hardened Material: Heat to 25F(15C) below original tempering temperature, hold two hours, cool in still air.

Welding

Use 440C or 420 stainless steel filler material. Annealed Material: Preheat 600/800F(320/430C), maintain over 600F(320C) during welding. Reanneal or temper 1200/1400F(650/760C) for 4 hours after welding.

Hardened Material: Preheat to 50F(30C) below original tempering temperature (400F (205C) minimum). Maintain above 400F(205C) during welding. Cool to 150F(65C) after welding. Temper immediately 25F(15C) below original tempering temperature. Minimum 400F(205C)

Physical Properties

Modulus of Elasticity30psix10(6)(200 GPa)
Density0.278 lb/in3(7640 kg/M3)
Thermal Conductivity14.0 BTU/hr./ft./F 24.2 W/m/ °K) 
440C Physical Properties
Physical properties for grade 440 stainless steels.
Grade Density (kg/m3) Elastic Modulus (GPa) Mean Coefficient of Thermal Expansion (mm/m/C) Thermal Conductivity (W/m.K) Specific Heat
0-100C (J/kg.K)
Electrical Resistivity (nW.m)
0-100C 0-200C 0-600C at 100C at 500C
440A/B/C 7650 200 10.1 10.3 11.7 24.2 - 460 600
 Machining
In the annealed condition this grade is relatively easily machined; approximately the same as for high speed steel. If this grade is hardened machining becomes very difficult and probably impossible.

Source:  http://www.multiplex-trd.com/articles/about_440c_steel.htm
             http://www.simplytoolsteel.com/440C-stainless-steel.html

Comments :

3 Comments to “ASTM A276-98b, AISI 440C Stainless Steel Data Sheet: Composition, Applications and Properties”

Anonymous said... on 

DEAR SIR,
KINDLY QUOTE US FOR THE ROUND BAR REQUIRED BELOW
WE WOULD ALSO BE INTRESTED IN YOUR SURPLUS STOCK


STAINLESS STEEL ROUND BAR
GRADE - AISI 440C (AS PER CHEMICAL COMPOSITION)


REQUIREMENT AS FOLLOWS:-

DIAMETER : 20M.M – 1 M.T
25M.M - 2 M.T
32M.M - 3 M.T
36 M.M - 3 M.T
40 M.M – 3 M.T
45 M.M - 3 M.T
50 M.M - 3 M.T
55 M.M – 2 M.T
65M.M – 2 M.T
70M.M – 2 M.T
75M.M – 2 M.T
80 M.M – 2 M.T
90 M.M – 2 M.T


LENGTH : 4 - 6 MTR
TOTAL QUANTITY : 20 - 30 M......T
TOL : 0.2 - / 0.2 +
FINISH : BRIGHT BAR
GRADE : AISI 440C


WE REQUIRE THE FOLLOWING MATERIAL FOR MANUFACTIRING SEVERAL COMPONENTS FOR OUR COUSTOMER OVERSEAS SO ITS AN URGENT REQUIREMENT



TERMS :

CHEMICAL,MACHENICAL & ULTRASONIC TEST CERTIFICATE REQUIRED
MATERIAL WILL BE THE AS ASTM A276 GR 440C (CARBON - 0.95- 1.20 ) STANDARD
PAYMENT - AS PER YOUR TERMS (NO ISSUE)
CLEAN SURFACE WITHOUT ANY DENT OR CRACK







THANK YOU,
SATISH MEHTA
(PURCHASE MANAGER)
SAGAR STEEL CENTRE
(AN ISO 9001 - 2008 CERTIFIED CO)
CONTACT NO - 9769690405
TEL :- 022-23885555/66666677
MUMBAI , INDIA
MAIL : SAGARSTEELS@AOL.COM
WEBSITE : WWW.SAGARSTEELCENTRE.COM
WWW.SS440C.COMeo


Ashish Shah said... on 

347h SS Round Bar Manufacturers

Unknown said... on 

Awesome thoughts!

Stainless Steel 420 Round Bar Manufacturers

Post a Comment

If you have any questions, concerns, or feedback about our website, our team is always here to assist you.

 
© Copyright 2013 Search Steel